دانلود مقاله : Correlation between the capacitor performance and pore structure of ordered mesoporous carbons 2013
![دانلود مقاله : Correlation between the capacitor performance and pore structure of ordered mesopor](/content/productpic/15239f1c0c980-b627-45ce-8717-91a576c5dec5.png)
دانلود مقاله :
Correlation between the capacitor performance and pore structure of ordered mesoporous carbons 2013
نویسندگان :
Takatomo Matsui , Shunsuke Tanaka , Yoshikazu Miyake
فرمت: pdf
چکیده :
Mesoporous carbons were synthesized by organic–organic self-assembly of triblock copolymer F127 and
phenolic resin oligomers composed of resorcinol–formaldehyde or resorcinol–furfural. The mesostructure
control was performed by using different polymerization catalysts, ammonia and acetic acid. The
effects of the aldehyde and polymerization catalyst on pore architecture of mesoporous carbons were
investigated. Disordered mesostructure with poorly disconnected mesopores was formed using furfural.
In contrast, when formaldehyde was used, ordered structure with mesochannels was formed. In addition,
changes in mesochannel length and the degree of long-range order are found to depend on polymerization
catalyst. The porous carbons with different structure were used as a model material to investigate
the ion storage/transfer behavior in electrical double-layer capacitor. Electrochemical cyclic voltammetry
measurements were conducted in 1 Msulfuric acid electrolyte solution. The ordered mesoporous carbons
show superior capacitances and rate performance over the disordered carbons. Electrochemical impedance
spectroscopy was used to assess the transport properties. The impedance data clearly demonstrated
that the degree of long-range order and channel length can influence the ion transport, resulting in superior
capacitive performances.
?>